Materials
With an open printing system, you have the freedom to use any filament. Choose from Anisoprint materials, extended material profiles from Polymaker and eSun or use your own!
Anisoprinting Open System
3D print complex parts with
-
Flexible materials choice
-
Modify the fiber volume ratio
-
Multiple fiber laying trajectories
COMBINE
BASE FILAMENT
WITH
CONTINUOUS FIBER
OR
Anisoprint Plastic Filaments
SMOOTH PA is 10% carbon fiber reinforced PA12 filament, which provides improved
surface quality, strength and warping. Compared to other polyamide filaments on the
market, Smooth PA features low moisture absorption and anti-warping technology.
CFC PA is a non-filled Polyamide 12 developed by Polymaker for Anisoprint CFC (Continuous Fiber
Co-extrusion) technology. The low viscosity of the plastic ensures better adhesion between the fiber
layers, while the fast cooling and solidification rate helps to achieve better fiber placement.
This low water absorption plastic can be printed without a dryer.
Anisoprint Continuous Fibers
CONTINUOUS CARBON FIBRE + PETG | |
|---|---|
Effective Diameter (mm) | 0.35 |
Fiber Volume (%) | 60 |
Elastic Modulus (GPa) | 150 |
Tensile Strength (MPa) | 2200 |
Density, g/cm3 | 1.4 |
Tensile modulus in fiber direction (GPa) | 64 |
Poisson ratio 21 | 0.36 |
Tensile ultimate stress in fiber direction (MPa) | 860 |
Tensile elongation in fiber direction (%) | 1.3 |
Compressive ultimate stress in fiber direction (MPa) | 290 |
Flexural strength (MPa) | 520 |
CONTINUOUS BASALT FIBER + PETG | |
|---|---|
Effective Diameter (mm) | 0.28 |
Fiber Volume (%) | 60 |
Elastic Modulus (GPa) | 54 |
Tensile Strength (MPa) | 1557 |
Density, g/cm3 | 1.7 |
Tensile modulus in fiber direction (GPa) | 22 |
Poisson ratio 21 | 0.34 |
Tensile ultimate stress in fiber direction (MPa) | 600 |
Tensile elongation in fiber direction (%) | 1.2 |
Compressive ultimate stress in fiber direction (MPa) | 195 |
Compressive modulus in fiber direction (GPa) | 20 |
eSUN Plastic Filaments
Anisoprint have the following eSun filament profiles in their Aura software:
eSUN ePA Nylon
- Fire retardant (UL94-V2 flame retardant).
- Printing temp. is 230~260℃.
- Super strong.
eSUN PETG
- Combines the benefits of ABS (stronger, temperature resistant, more durable) and PLA (easy to print) in one material.
- High mechanical strength and excellent flexibility
- Excellent layer adhesion.
- Less warping and shrinkage.
- 100% recyclable
Printing Parameters:
- Print temperature: 240~255℃
- Bed temperature: 80~90℃
- Printing speed: 30~60mm/s
- Moving speed: 30~60mm/s